November 4, 2013

To Glaze or Not to Glaze. Oct/Nov Issue of My Molds Newsletter 2013

News that Inspires Imagination! The Preferred Place for Clay Push Molds. Aug/Sep 2013 Issue of My Molds Newsletter.
The Preferred Place for Clay Push Molds
Dear Readers,

Hey everyone! It's been a little while since our last newsletter, so it's about time we catch-up on the latest happenings around here. The temperatures are starting to get lower and you know what that means! Time to get in full swing into unleashing that creative energy that's been bursting to be put to good use! With just a little spark of imagination who knows what you can come up with, and if you let us we would be happy to help you get into your creative mood.

Did you realize that there's only seven full weeks left til Christmas?! Yes, I know you know the drill. Collect ideas, gather supplies and work like crazy to get things done before it gets too busy to enjoy the season. Let's look at this differently this year and take our time. Collecting idea can be so fun. Go to craft shows, visit Pinterest, watch the trends. Getting supplies online can eliminate the long lines, uninterested off-spring and unnecessary running around. Of coarse shopping at Mad About Molds is fun and easy. :) And it come time to work on your projects make it more like play time. Invites your friends, turn on a little music and have a few snacks near by and have a good time! So lets get inspired and make stuff!

Be sure to read this months article "To Glaze or Not to Glaze - That is the question!

Please take the time to sit back and enjoy this issue of My Molds!
 

All the best,
Marjorie with Mad About Molds
News that Inspires Imagination!



"It's a Fall for all"
 

Did you know we have over 1,000 molds to choose from?

That's more molds then anyone could ever need! Plus we offer many molds in both a hard molds and flexible molds. Both have their advantages which we will help you understand once and for all today.

There are differences in our hard and flexible molds and it’s good to think about how you are going to use them to know which kind to get. It depends mainly on the type of casting you choose to work with as to what type you should purchase.

Our hard molds (the kind found on all our shopping pages) are made of a clay that hardens when cured. They are very durable and can withstand a long life. If you look at our “basic instructions” on our website, you will see they work great with polymer clay as well as many other castings. Our easy instructions shows you how to use our molds with a perfectly flat back every time.

Our flexible molds (found on the flexible molds page) are made of a flexible clay that is slightly flexible and allows for the casting to be removed easily. However it is important that you are careful when removing the casting, because the movement can produce a deformed casting. Be sure to read the instructions on the flexible molds page on our website for more details. Also, you will want to be sure to choose the flexible option when you are ordering from the flexible page.
 

We make these molds individually one-by-one, each handmade mold is inspected and needs to meet our high standard before shipping to you. Our unique process insures a clean, smooth and uniform mold. The items that we choose to mold are based on minimal undercuts when being molded, insuring you a quality casted piece.

I hope this helps and if you have any other questions feel free to email us anytime.
 


 

Why Molds are a Great Value!

In a tough economy, people look for ways to save money. Molds can be a great value to you, by allowing you to create a multitude of castings with just one mold. Also consider the many ways to use molds on our “Creative Ideas Page” to get the most out of your molds.

Here’s just a few reasons why molds are a great value.
  • Save by making your own embellishments, instead of purchasing them new.
  • Save by making an endless supply of castings for your favorite projects.
  • Save by staying home, instead of going out for your entertainment and relaxation.
  • Save by selling your creations, as an extra income for your family.
  • Save by using many everyday items found around your house as molding tools.
  • Save by creating personal gifts, instead of purchasing store bought.
     


A Season of Colorful Equilibrium

Pantone Fashion Color Report Spring 2014
 
Designers take a modern twist on the traditional for spring 2014 by pairing soft pastels with vivid brights to create a colorful equilibrium. Inspired by a mixture of blooming flowers, travels abroad and strong, confident women, designers use color to refresh, revive and defy conventional wisdom. "This season, consumers are looking for a state of thoughtful, emotional and artistic equilibrium," said Leatrice Eiseman, executive director of the Pantone Color Institute®. "While this need for stability is reflected in the composition of the palette, the inherent versatility of the individual colors allows for experimentation with new looks and color combinations."

Three very adaptable pastels sit on one end of the palette, and, because we are so accustomed to seeing them as nature's background, they can be creatively combined with any other color in the spectrum. Placid Blue, like a picture-perfect, tranquil and reassuring sky, induces a sense of peaceful calmness, while Violet Tulip, a romantic, vintage purple, evokes wistful nostalgia. Similar to the verdant shade of springtime foliage, Hemlock, a summery, ornamental green, provides a decorative touch that's very different from the greens of recent seasons. Pair any of these versatile pastels with a bolder hue for an au courant look.

Sand, a lightly toasted and amiable neutral, conjures images of the beach and the carefree days of summer. Try pairing Sand with Hemlock for perfect, natural balance. Paloma serves as a quintessential neutral, interesting enough to be worn alone or combined with any color for sophisticated poise.

Cayenne, a high-pitched red, adds a dash of spicy heat to neutrals, and heightens the excitement when mixed with Freesia, a blazing yellow that is sure to illuminate wardrobes this season. A tropical, floral-inspired shade, Freesia's warmth and energy help set the stage for Celosia Orange, an optimistic, spontaneous hue. Pair Celosia Orange with Violet Tulip for a captivating vision, much like the setting summer sun.

The palette is brought full circle with Radiant Orchid, a bold counterpart to Violet Tulip, and Dazzling Blue, a scintillating, polar opposite to Placid Blue. Surprisingly, these strong, vibrant colors also pair well across the palette: They are perfect companions to pastels, and add confidence and vivacity when mixed with other bold colors.

For more than 20 years, Pantone, the global authority on color, has surveyed the designers of New York Fashion Week and beyond to bring you the season's most important color trends. 



 




To Glaze or Not to Glaze - That is the Question!

This all depends on the type of finish you want. A lot of polymer artists prefer their pieces to be natural and unglazed. I prefer that at times myself -- it all depends on the individual piece and the finished look I'm aiming for. You can get a nice sheen by buffing with a soft cloth or towel and you can also get a high shine if you buff with some sort of buffing wheel. If you are aiming for this... your piece needs to have a very smooth finish. This involves sanding your work with different grits of wet/dry sandpaper. I have also found that the smoother your clay is before baking, the less sanding you will have to do afterwords. Some people finish with 1000 grit sandpaper, others go up to 1500 or 2000. I have found that there isn't too much difference in smoothness or shine above 800 grit so it is all a matter of what clay you are working with and your own preference.
Then there is the type of buffing wheels to use. Some of our clay colleagues had fabulous buffing machines that were to drool over but we decided to go simply and make more use of the tools like our dremel, we already had. I read up on Desiree McCrory's site about her new buffing pad and so we went on a hunt to find the right fabric to make our own. It is a simple concept but does a beautiful job and leaves a really high sheen! We use a drill press stand so it frees both hands to buff making it easier and safer to use.
To Glaze ..... the How and Why.....
So if you prefer to glaze your pieces, many have asked which one do you use and what works best. This is something that is a little different for everyone but I will share with you what we have learned from our past experiences.
Some polymer clay techniques using inks, mica powders or chalks, require some sort of glaze finish in order to protect them from wearing off. One of the newest type of glazes that polymer clay artists have discovered is the PYM11 (Preserve Your Memories 11). This is amazing stuff and works well as a sealing agent, especially if you are using inks or mica powders. It leaves a soft matte finish so if you prefer your piece to be glossy, you can use PYM11 as a sealer and then coat with Future acrylic afterwords.
PYM11 is only available as an aerosol spray so is a more difficult to use on smaller type beads. It also has a very strong odor so you will want to use this outdoors in the fresh air so you do not breathe in the fumes.
How to Use: Lay your pieces out onto a paper lined tray. Spray your pieces very lightly. Allow to dry (a few minutes) and then turn your tray around so you are spraying from the opposite direction and give a light spray again. Turn your pieces over and repeat for the other side.
Pro: Makes a great sealer when using mica powders, chalks and especially inks.
Con: Only available in an aerosol spray so is a little more difficult to use on smaller type beads.
Type of Finish: soft matte
Diamond Wood Finish by Flecto is the only type of varathane we consider safe to use with your polymer clay. We have tried various other brands (such as Minwax acrylic) and discovered they are not all the same. They would peel and wear off and I'm glad we only experimented with them in a small way first.
The Diamond by Flecto is available in glossy, semi-gloss and satin finishes. It is also available in an aerosol spray which is great for larger type surfaces. In many of our pieces like our animal prints, we prefer to use semi-gloss as it actually gives more of a soft satin gloss look and isn't overly shiny. I fill a small jar to use from instead of using it straight from the can. If it gets a little too thick, you can add a little water to thin it out and it will apply much easier.
How to use: A good quality clean soft paintbrush is the key. If you do not use a good brush or have too much varathane on your brush, it will cause streaks. Apply several very thin coats, allowing to dry thoroughly in between. You might still notice a bit of streaking after the first coat but that will eventually lesson after each application. After your pieces are dry, you can harden your finish a little more by baking your pieces at 200 F for 12-15 minutes. This also helps get rid of any small streaks that might still be showing.
Pro: Dries very quickly between coats and leaves a nice finish.
Con: Not so good on items with a lot of mica powder, chalks or inks as a sealer.
Type of Finish: semi-gloss to satin
The other type of glaze I like to use is Future -- which is now called Pledge with Future. This is our preference when we want our pieces to have a permanent high shine. We especially prefer to use it on pieces that require more wear and tear like pens or mirror compacts. If our pieces have mica powders, inks or chalks applied, we generally spray them first with the PYM11 and then coat with Future to add the shine and add a little more protection.
How to use: You can use a clean soft paintbrush or some people like to use q-tips. Both work great! Apply several thin coats, allowing to dry thoroughly in between. Future takes a little longer to dry so takes a little more patience. I found that if you apply the next coat too soon, it leaves a lot of streaks so I have to wash it off or sand it and start all over so is best to allow to dry completely.
You can also harden your finish more by baking again afterwords at 200 F for 12-15 minutes. This also helps to bring out a little more shine.
Pro: Makes a good hard finish and works well for sealing pieces when using mica powders, chalks, etc. as well as long wearing items such as pens. Also a very pleasant smell.
Con: Very time consuming as several coats need to be applied with lots of drying time between coats.
Type of Finish: glossy to super glossy
Just a note: I had read not to dip your pieces in future but have had several people contact me lately telling me they've had great success with that so I am reviewing that option and will have to experiment for myself with that more.
I hope this helps answer some questions you might have regarding finishing your pieces.




 




 

Fun Links:
Mobile Site
  

 Contact Us!

 Comments Welcomed!
 How are we doing?
 Let us know what you are thinking!
 www.MadAboutMolds.com

The Preferred Place for Clay Push Molds!
 
When it comes to service, we break the mold!
Thank You!
Copyright © 2013 Mad About Molds, All rights reserved.
Email Marketing Powered by MailChimp
 unsubscribe from this list | update subscription preferences

Feel free to send this newsletter to a friend. If you received this newsletter from a friend feel free to sign up for our newsletter. We don't want to lose touch with you! We will not sell, trade or give away your personal information or email address.